Ultrafast laser structuring of graphene-based multi-zone heaters for the detection of antioxidant capacity

Zhao Chi Chen, Shih Feng Tseng, Tien Li Chang, Wen Tse Hsiao, Yung Sheng Lin

研究成果: 雜誌貢獻文章同行評審

1 引文 斯高帕斯(Scopus)


This study presents a non-contact processing method of heating devices using maskless ultrafast laser direct structuring of graphene (G) films coated on the alumina ceramic (Al2O3) substrates for antioxidant capacity (ATC). The effect of ATC temperatures on the electrode structures of the electrical resistance and electromechanical properties of G-based multi-zone (GM) device was investigated. The fabricated GM device with four electrode structures could be regarded as an on-site heater in assisting preheating treatment. The required laser processing parameters of energy fluence, pulse repetition rate, and scanning speed were 7.02 J/cm2, 300 kHz, and 500 mm/s, respectively. For the GM heater, a steady-state temperature of 100 °C could be reached within 10 s under a lower applied voltage of 14 V. The experimental results demonstrated that the electrothermal performance of GM devices was used to control the ATC preheating process. The absorbance values of ATC ranged from 0.5 ± 0.01 to 1.07 ± 0.04 measured by a spectrophotometer at a wavelength of 700 nm. Moreover, the absorbance value increased with increasing concentration of standard solution that the high absorbance represented the ATC solution with high reducing power. Successful operation of GM heater with a simple and promising technique should find application in laser-ablated G electrodes for an advanced inspection instrument of ATC.
頁(從 - 到)3115-3124
期刊International Journal of Advanced Manufacturing Technology
出版狀態已發佈 - 8月 2019

ASJC Scopus subject areas

  • 控制與系統工程
  • 軟體
  • 機械工業
  • 電腦科學應用
  • 工業與製造工程


深入研究「Ultrafast laser structuring of graphene-based multi-zone heaters for the detection of antioxidant capacity」主題。共同形成了獨特的指紋。