Photocatalytic properties of nanocrystalline TiO2 thin film with Ag additions

Chung-Chieh Chang, Chung Kwei Lin, Chih Chieh Chan, Chao Sheng Hsu, Chin Yi Chen

研究成果: 雜誌貢獻文章同行評審

66 引文 斯高帕斯(Scopus)

摘要

In the present study, nanocrystalline TiO2/Ag composite thin films were prepared by a sol-gel spin coating technique. While, by introducing polystyrene (PS) microspheres, porous TiO2/Ag films were obtained after calcining at a temperature of 500°C. The as-prepared TiO2 and TiO2/Ag thin films were characterized by X-ray diffractometry, and scanning electron microscopy to reveal the structural and morphological differences. In addition, the photocatalytic properties of these films were investigated by degrading methylene blue under UV irradiation. After 500°C calcination, the microstructure of PS-TiO2 film without Ag addition exhibited a sponge-like microstructure while significant sintering effect was noticed with Ag additions and the films exhibited a porous microstructure. Meanwhile, coalescence of nanocrystalline anatase-phase TiO2 can be observed with respect to the sharpening of XRD diffraction peaks. The photodegradation of porous TiO2 doped with 1 mol% Ag exhibited the best photocatalytic efficiency where 72% methylene blue can be decomposed after UV exposure for 12 h.
原文英語
頁(從 - 到)274-278
頁數5
期刊Thin Solid Films
494
發行號1-2
DOIs
出版狀態已發佈 - 1月 3 2006
對外發佈

ASJC Scopus subject areas

  • 電子、光磁材料
  • 表面和介面
  • 表面、塗料和薄膜
  • 金屬和合金
  • 材料化學

指紋

深入研究「Photocatalytic properties of nanocrystalline TiO2 thin film with Ag additions」主題。共同形成了獨特的指紋。

引用此