Microwave absorbing properties of iron nanowire at x-band frequencies

Ruey Bin Yang, Wen Fan Liang, Wei Syuan Lin, Hong Ming Lin, Chien Yie Tsay, Chung Kwei Lin

研究成果: 雜誌貢獻文章同行評審

27 引文 斯高帕斯(Scopus)


Iron nanowires and nanoparticles are fabricated via the reduction of iron salts (FeCl 36H 2O) with or without a parallel magnetic field, respectively. Polyvinyl pyrrolidone was added during the reduction process and formed a thin passive layer to minimize the oxidation. The as-obtained iron nanomaterials were then used as magnetic fillers, added to an epoxy resin, and iron nanoparticle or nanowire composites were prepared. The complex permittivity (ε′-jε″) and permeability (μ ′-jμ″) of these composites are measured by a cavity perturbation method from 7 to 14 GHz. The iron nanowire composites exhibited superior microwaving absorbing properties compared to iron nanoparticle composites. The optimal absorption peak of iron nanowire composites reached -10.5 dB (>90% power absorption) and -15.5 dB (>97% power absorption) with a thickness of 2 and 3 mm, respectively.
期刊Journal of Applied Physics
出版狀態已發佈 - 4月 1 2011

ASJC Scopus subject areas

  • 物理與天文學 (全部)


深入研究「Microwave absorbing properties of iron nanowire at x-band frequencies」主題。共同形成了獨特的指紋。