Extensive void defects in mesoporous aluminosilicate MGM-41

Hong Ping Lin, She Tin Wong, Chung Yuan Mou, Chih Yuan Tang

研究成果: 雜誌貢獻文章同行評審

170 引文 斯高帕斯(Scopus)


Mesoporous MCM-41 materials with a distinct N2-sorption hysteresis behavior have been prepared from pure silica and aluminosilicate - C16 trimethylammonium (TMA)Br systems by a delayed neutralization procedure. On the basis of the analysis of transmission electron microscopy micrographs of these MCM-41 materials, we observed that the sample with large type-H4 hysteresis loop at p/p0 between 0.5 and 1.0 contains extensive structural defect holes amid the nanochannels. These holes are irregular in shape and their size distributes between 5.0 and 30.0 nm. The pore-blocking effect leads to the hysteresis in desorption. Aluminosilicate MCM-41 often possesses a larger hysteresis loop than pure silica MCM-41. The linear channel system of MCM-41 becomes effectively interconnected through these defect holes. The unusual adsorption hysteresis is associated with the pore-blocking effect around the embedded voids in the framework structures. The size of the adsorption-desorption hysteresis loop is proportional to the volume of hole defects in the nanochannels, and it is dependent on the synthesis conditions such as water content, Si/Al ratio, and morphology. Tubular morphology is often associated with large hysteresis behavior and thus more hole defects. The interconnecting channels through defect holes thus makes the diffusion of molecules inside the MCM-41 structure more effective, which is important in catalysis applications.

頁(從 - 到)8967-8975
期刊Journal of Physical Chemistry B
出版狀態已發佈 - 9月 28 2000

ASJC Scopus subject areas

  • 物理與理論化學
  • 表面、塗料和薄膜
  • 材料化學


深入研究「Extensive void defects in mesoporous aluminosilicate MGM-41」主題。共同形成了獨特的指紋。