Enhanced energy storage ability of UIO66 active material on acid-treated carbon cloth for flexible supercapacitors

Yun Han Hung, Lu Yin Lin, Hung Yun Lin, Yu Shun Sung, Yu Jui Hsiao, Yi Chiun Li

研究成果: 雜誌貢獻文章同行評審

16 引文 斯高帕斯(Scopus)

摘要

Metal organic framework, UIO66, has been regarded as one of potential electroactive materials for supercapacitors (SC), due to high surface area and tunable pore structures. To further improve electrochemical performance of UIO66-based SC, morphology design of UIO66 is necessary. In this work, it is the first time to study the effects of pH value of precursor solution on physical and electrochemical properties of UIO66. The pH values of 1, 2, 4 and 6 of precursor solution is prepared using acetic acid which is also acts as structure-directing agent. The different sizes of UIO66 are obtained by merely changing pH value of precursor solution. The UIO66 octahedron synthesized using pH values of 1 and 6 present the smallest size and similar dimensions to carbon black with irregular spherical morphology and size of around 75 nm which is also in paste. Carbon cloth (CC) substrate is also modified using acid to understand substrate influences on SC performance. The optimized pH value of 1 and 6 is respectively obtained for synthesizing UIO66 on acid-treated CC (ACC) and CC substrates. Due to the extra energy storage from substrate, the electrode with UIO66 prepared using pH value of 6 on ACC (M6/ACC) shows the highest areal capacitance (CA) of 3.87 mF/cm2 at 2.5 A/g. Also, the symmetric SC (SSC) fabricated using M6/ACC electrodes and aqueous medium-based electrolyte shows potential window of 0.9 V, maximum energy density of 36 mWh/kg at 89.94 W/kg, and CA retention of 130% after 10000 times charging and discharging process.
原文英語
文章編號138241
期刊Electrochimica Acta
380
DOIs
出版狀態已發佈 - 6月 2021

ASJC Scopus subject areas

  • 一般化學工程
  • 電化學

指紋

深入研究「Enhanced energy storage ability of UIO66 active material on acid-treated carbon cloth for flexible supercapacitors」主題。共同形成了獨特的指紋。

引用此