Comparative analysis of bonding strength between enamel and overlay of varying thicknesses following an aging test

研究成果: 雜誌貢獻文章同行評審

3 引文 斯高帕斯(Scopus)

摘要

Background/purpose: Overlay restorations can be used clinically as a treatment option to preserve natural dentine. However, whether the residual enamel thickness and overlay thickness affect the adhesion between the restoration and tooth is still unknown. This study was to investigate effects of the overlay thickness and residual enamel thickness on bonding strength. Materials and methods: Overlays of different thicknesses were prepared with natural teeth which had 2, 4, and 6 mm of occlusal reduction (n = 10). Specimens were subjected to 10,000 cycles in water at 5–55 °C, and finally compressive strength tests were used to evaluate the bonding strength. Results: All groups showed good bond strength (P > 0.05). The overlay restorations of different thicknesses reduced the preparation amount by 30.3%–7.2% and significantly preserved more of the tooth structure (P < 0.005). Compared to the control group, the overlay restoration increased the marginal fitness by about 0.67–0.88 times. The thermal cycling indicated that the decrease in the maximum bearing stress was due to the aging of the ceramic itself. Therefore, the thickness of the overlay had a greater influence on the compressive strength than the bond strength. Conclusion: Based on the above this study recommends an overlay thickness of at least 2 mm in clinical practice. The aging test confirmed that adhesion between the overlay and teeth was quite firm and stable. This shows that a stable adhesive effect of the overlay can be used as a treatment option for preserving a greater amount of a tooth's structure.
原文英語
頁(從 - 到)1850-1858
頁數9
期刊Journal of Dental Sciences
18
發行號4
DOIs
出版狀態接受/付印 - 2023

ASJC Scopus subject areas

  • 一般牙醫學

指紋

深入研究「Comparative analysis of bonding strength between enamel and overlay of varying thicknesses following an aging test」主題。共同形成了獨特的指紋。

引用此