Characterization of elecrophoretically deposited nanocrystalline titanium dioxide films

C. K. Lin, T. J. Yang, Y. C. Feng, T. T. Tsung, C. Y. Su

研究成果: 雜誌貢獻文章同行評審

50 引文 斯高帕斯(Scopus)


In the present study, nanocrystalline TiO2 powders were electrophoretically deposited on the surface of a stainless steel substrate. Post heat treatment at 600 or 800 °C was performed to improve the adhesion strength. The as-prepared and heat-treated samples were characterized by atomic force microscopy (AFM), scanning electron microscopy (SEM), X-ray diffraction (XRD), and synchrotron X-ray absorption spectroscopy. Experimental results show that the as-deposited nanocrystalline TiO2 films exhibited anatase phase. Heat treatment at 600 °C not only retained the original nanocrystalline TiO2 anatase phase but also increased the adhesion strength of the film. Anatase to rutile transformation was observed when the TiO2 films were heat-treated at 800 °C. Crack formation due to the phase transformation was also noted and further decreased the adhesive properties of the TiO2 films.
頁(從 - 到)3184-3189
期刊Surface and Coatings Technology
發行號10 SPEC. ISS.
出版狀態已發佈 - 2月 24 2006

ASJC Scopus subject areas

  • 表面、塗料和薄膜
  • 凝聚態物理學
  • 表面和介面


深入研究「Characterization of elecrophoretically deposited nanocrystalline titanium dioxide films」主題。共同形成了獨特的指紋。