Application of Aluminum Nitride Thin Film on Biosensing of Cell Differentiation

Keng Liang Ou, Chang Chih Chen, Che Tong Lin, Chin Sung Chen, Chia Cheng Lin, Sheng Yang Lee

研究成果: 雜誌貢獻文章同行評審

6 引文 斯高帕斯(Scopus)


The microstructural properties and functional failure of Al-N thin films metal-insulator-metal (MIM) capacitors fabricated by reactive-sputtering were studied for the application as differential biosensing of bone cell. The film properties and capacitor capability of Al-N films with and without cell culture were determined using glancing incident X-ray diffraction, leakage current density, cross-sectional transmission electron microscopy, and stress analysis as well as biocompatibility test. The as-deposited Al film has a face-center cubic structure and a low resistivity of 3.21 μ cm. With increasing nitrogen concentration of Al-N films, phase transformations are identified as fcc-Al→fcc-Al (N) →fcc-AlN→hcp-AlN. As the testing result of MIM capacitor, it was shown that the failure of the AlN MIM capacitors was caused by microvoids formed on the film after cell culture. The microvoid having occurred at the cell/AlN MIM capacitor caused it to leak out much of the current to the extent of a few microamperes even at 150 kVcm. The formation of microvoid and low break down voltage were explained by the stress variation during the cell differentiation and proliferation. The stress induced by interaction bone cell and hcp-AlN film resulted in lattice and/or atomic displacement and distortion of AlN. It is believed that the [002] oriented AlN film is shown to perform effectively as a biosensing film to detect the cell differentiation and proliferation by MIM capacitor device. Furthermore, the biosensing film will have a potential for use in wireless technology to monitor the osseointegration in the future.
頁(從 - 到)P11-P15
期刊Journal of the Electrochemical Society
出版狀態已發佈 - 2007

ASJC Scopus subject areas

  • 電子、光磁材料
  • 材料化學
  • 表面、塗料和薄膜
  • 電化學
  • 可再生能源、永續發展與環境


深入研究「Application of Aluminum Nitride Thin Film on Biosensing of Cell Differentiation」主題。共同形成了獨特的指紋。