A novel strategy for an environmentally friendly etching process is proposed based on the vapor from hot electron-activated (HEA) water, in which, HEA water with a weakly hydrogen-bonded structure is neutral. Compared to the vapor from deionized (DI) water, the vapor from HEA water exhibits a facile etching process to a glass sheet after exposing it to vapor at room temperature. The etched glass sheet demonstrates a granular surface morphology with a hydrophobic structure. In addition, the resulting nanostructured glass shows a uniform signal intensity of surface-enhanced Raman scattering (SERS) of rhodamine 6G (R6G). This is favorable for developing reliable sensors. The adhesion of deposited metals on the etched glass is also enhanced. Furthermore, the distortion and reformation of the deposited gold nanoparticles (AuNPs) by vapor from HEA water were observed. It suggests that this vapor has higher energy than conventional DI water does. This innovative concept has emerged as a promising strategy for environmentally friendly nanostructured etching.

Original languageEnglish
Pages (from-to)3098-3105
Number of pages8
JournalGreen Chemistry
Issue number10
Publication statusPublished - 2016

ASJC Scopus subject areas

  • Environmental Chemistry
  • Pollution


Dive into the research topics of 'An environmentally friendly etching agent: Vapor from hot electron-activated liquid water'. Together they form a unique fingerprint.

Cite this